Method For Producing Functionalized Thermoplastic Elastomers

ABSTRACT

A method for producing functionalized thermoplastic elastomers on the basis of grafting substrates, selected from olefine-block copolymers of composition 80 to 98 mass-% ethylene-/2 to 20 mass-% C 3 - to C- 12 -olefine units or partially crystalline propylene/ethylene and/or C 4 - to C- 12 -olefine and/or C 4 - to C 12 -diene-copolymers of composition 50 to 98 mass-% propylene-/2 to 50 mass-% C 2   , - and/or C 4 - to C 12 -olefine and/or C 4 - to C 12 -diene units or cross-linked styrene/define/styrene or styrene/olefine-block copolymers, wherein, in a liquid mixing reactor per 100 mass parts of particular grafting substrate—0.1 to 15 mass parts of at least one functional monomer from the series of functional groups comprising α,β-ethylenic unsaturated compounds or 0.1 to 15 mass parts of a monomer mixture comprising at least one of said functional monomers and—0.01 to 10 mass parts of at least one initiator forming free radicals having a 1-hour half-life temperature (T Hwz/1h ) between 50 and 200° C. are added and, at reaction temperatures between 40° C. and the melting or softening temperature of the grafting substrate, are polymerized over a reaction period between 10 and 200 min to solid-fluid phase, wherein a grafting product having a grafted functional monomer is produced by such a solid phase functionalization which is used as an input component for further processing. Functionalized thermoplastic elastomers having a degree of functionalization between 0.1 and 5 mass-% can be obtained using the method. Said elastomers are suitable for use as a bonding agent and/or adhesive agent for various substrates or multi-layer composites.

The invention relates to a process for preparing functionalized thermoplastic elastomers based on graft substrates selected from

-   -   olefin block copolymers having the composition from 80 to 98         mass-% of ethylene-/2 to 20 mass-% of C₃- to C₁₂ olefin units,         or     -   semi-crystalline propylene/ethylene and/or C₄- to C₁₂ olefin         copolymers and/or C₄- to C₁₂ diene copolymers of the composition         50 to 98 mass-% of propylene-12 to 50 mass-% of C₂- and/or C₄-         to C₁₂- olefin units and/or C₄- to C_(12—) diene units, or     -   cross-linked styrene/olefin/styrene- or styrene/olefin-block         copolymers.

For numerous applications, particularly as compatibility or adhesion promoter (adhesive agent), statistical (random) and heterophasic (impact) propylene copolymers (RCP, HCP), ethylene/propylene copolymers (EPM) or ethylene!propylene/diene terpolymers (EPDM) containing carboxylated olefin polymers based on polyethylenes of different density (LDPE, MDPE, HDPE), ethylene/α, β-ethylenically unsaturated C₃- to C₁₂ olefin copolymers (LLDPE, POE) or propylene-homo(HPP) and C₂- and/or C₄- to C₁₂ olefin units are used. The aforementioned polymers are generally produced by means of reactive extrusion at high temperatures (150 to 300° C.) by grafting on the olefin backbone polymer an α, β-ethylenically unsaturated mono- or dicarboxylic acid or the anhydride thereof, particularly methacrylic acid, fumaric acid, and preferably maleic anhydride (MA), in the presence of a free-radical-forming peroxidic initiator. The above-described prior art can be found, inter alia, in the WO 91/18053 A1 U.S. Pat. No. 4,174,358 A, U.S. Pat. No. 4,537,929 A, U.S. Pat. No. 4,684,576 A, U.S. Pat. No. 4,751,270 A, U.S. Pat. No. 4,927,888 A, EP 0 266 221 B1, EP 0 287 140 B1, EP 0 403 109 A2, EP 0 467 178 B1, EP 0 581 360 51, EP 0 696 303 51, EP 0 878 510 51, U.S. Pat. No. 6,884,850 52, U.S. Pat. No. 2006/0211825 A1 and WO 2008/079784 A2.

In the same way, the corresponding functionalized olefin polymers are obtained by grafting α, β-ethylenically unsaturated compounds containing hydroxyl, epoxy, amino, imido, silane groups and other functional groups.

Increasingly, highly effective, non-cross-linked olefin elastomers composed of predominantly ethylene and/or propylene units produced by using special metallocene catalyst systems or random copolymers containing predominantly isotactic propylene sequences and about 8 to 32 mole % ethylene units are used as backbone polymers for functionalizing monomers having functional groups by grafting (functional monomers). The non-cross-linked olefin elastomers include especially ethylene-α-olefin block copolymers, such as the Infuse™ types from Dow Chemical Company. Examples for the random copolymers containing about 8 to 32 mole % ethylene units are the Vistamaxx™ types described in the documents U.S. Pat. No. 6,884,850 B2, U.S. Pat. No. 2005/0176888 A1, U.S. Pat. No. 2006/0199930 A1 and U.S. Pat. No. 2006/0211825 A1 from ExxonMobil Chemical Company or the Versify™ types from Dow as well as Notio™ types. The aforementioned types of ethylene-α-olefin block copolymers and random copolymers from the Dow Chemical Company are described in the documents U.S. Pat. No. 2006/0199914 A1 , WO 2006/102016 A2 and WO 2008/080111 A1 . The employed functional groups include, among others, carboxyl- or anhydride-, as well as hydroxyl- or epoxy-, amino-, imido- or silane-groups. The employed monomers with functional groups particularly frequently include α, β-ethylenically unsaturated mono- or dicarboxylic acids or their anhydrides (carboxyl monomers), for example, maleic anhydride.

Graft-carboxylation or graft-maleation performed at low reaction temperatures, i.e. below the melting or softening point of the olefin backbone polymer (graft substrate) in a solvent is, due to the technologically very complex polymer dissolution and in particular due to the solvent separation and solvent recovery necessary and the required graft product purification after grafting, not an economic alternative to the melt-grafting of acid (anhydride)- or other functional monomers on graft substrates composed of predominantly olefin units. Conversely, the functionalization of olefin polymers carried out in a solid-fluid polymer phase, particularly a carboxylation or maleation, are based on an economic technology study carried out below the melting or softening temperature of the graft substrate. This is known from the documents DD 275 160 A3, DD 275 161 A3, DO 300 977 A7, DE 41 23 972 A DE 43 42 605 A1, EP 0 469 693 B1 and EP 0 370 753 B1.

Suitable backbone polymers for this graft-functionalization (solid state grafting) carried out in the solid phase are semi-crystalline olefin polymers, which allow high diffusion rates of low molecular weight compounds in the amorphous phase formed between its glass-transition and melting point, with unsaturated carboxylic acids or anhydrides being among the low molecular weight compounds. High diffusion rates for low molecular weight compounds are one of the prerequisites for high graft-polymerization velocities.

Amorphous and low-crystalline olefin elastomers with special morphology, in particular elastomenc olefin segments containing styrene/selectively hydrogenated diene/(styrene) multi-block copolymers, can also be used as the polymer backbone for the free-radical solid-phase graft modification under certain polymerization conditions, see documents EP 0 642 538 61, EP 0 805 827 B1 and WO 2004/048426 A2, without achieving the required properties for use as a highly effective adhesives, including adhesion promoters for demanding metal/plastic and other multi-layer composites.

Frequently used adhesion promoters include, besdes carboxylated or maleated high-density polyethylenes with the abbreviation HDPE, or carboxylated branched low-density polyethylenes, with the abbreviation LOPE, especially low-density carboxylated linear ethylene copolymers, furthermore random propylene/ethylene copolymers composed predominantly of propylene units and lastly also styrene/selectively hydrogenated diene segment/styrene or styrene/selectively hydrogenated diene segment block copolymers, with the abbreviation TPE-S, containing “elastomeric” olefin units, which are the purpose of their carbonation, especially maleation, produced mostly by melt grafting, as described, for example, in the publications U.S. Pat. No. 5,346,963 A, U.S. Pat. No. 6,384,139 61, U.S. Pat. No. 6,331,592 B1, U.S. Pat. No. 6,884,850 B2, DE 198 41 303 A1, WO 01/92357 A1, WO 98/42760 A1, EP 0 659 784 61, U.S. Pat. No. 4,578,829 A, EP 0 173 380 A1 EP 0 085 115 B1 EP 0 371 001 B1 and EP 0 642 538 B1, and which can be used as adhesives for various applications, as disclosed in the documents

EP 0 696 303 81, EP 0 754 731 B1 and EP 0 878 510 Bl. The carboxylated linear ethylene copolymers either have a low C₃- to C₁₂-olefin co-monomer fraction below 15 mass-%, i.e. LLDPE, or a higher C₃- to C₁₂-olefin co-monomer fraction above 15 mass-%, referred to by the acronym POE. Carboxylated linear ethylene copolymers include, for example, special ethylene/octene (C₅) copolymers, referred to by the acronym EOC.

Moreover, bonding resins using mixtures of crystalline polyolefin, for example HDPE or LLDPE, and an amorphous or poorly crystalline olefin polymer, for example ethylene/propylene rubber with the abbreviation EPM, that were graft-carboxylated in the melt, are known and described in the publication EP 0 501 762 Bl.

The known melt-grafted olefin thermoplastic elastomers disadvantageously have low levels of bonded functional groups. A low grafted functional monomer fraction is thus present, i.e. a low degree of functionalization. Another drawback is the technical/technological and expensive measures for the removal of the high residual monomer fractions from the melt.

A process for preparing functionalized polypropylenes with polypropylene by radical grafting with low molecular weight compounds having functional groups under solid phase reaction conditions is known from DE 199 14 146 A1. In this process, the grafting of compounds having functional groups on polypropylene is carried out by continuously feeding the reactants and by continuously removing the reaction product in the temperature range between 80 and 160° C. The method is used, among other things, to improve the adhesion of polypropylene to mineral reinforcing materials.

DE 10 2007 030 801 A1 describes thermoplastically processable carboxylated styrene-olefin block copolymer/polyolefin compositions with a melt volume rate of MVR (230° C./5 kg) between 1 to 300 cm³/10 min and a fraction of grafted α, β- olefinally unsaturated mono- and/or dicarboxylic acid and/or of its anhydride in proportion to the entire polymer mass of between 0.3 and 5 mass-%. The melt-processable carboxylated styrene-olefin block copolymer/polyolefin compositions can be used as an adhesion promoter in coatings on different surfaces, in laminates and composites.

DE 196 07 430° C.1 discloses a continuous process for the modification of polyolefins in the solid phase. The modified polyolefins, for example styrene-modified polypropylene, can be prepared by a continuous process in which unsaturated monomers and thermally decomposing radical formers are absorbed from the gas phase by using polyolefin particles, and wherein the polyolefin particles in which the thermally decomposing free-radical generators and unsaturated monomers are absorbed, are exposed to a high-frequency field having a frequency of 2.4 to 2.5 GHz. The modified polyolefins are suitable for producing films, sheets, coatings, pipes, hollow bodies, foams and molded materials.

A method producing carboxylated ethylene polymer blends is known from WO 2009/033465 A2. In a first stage 0.05 to 15 mass parts of an α, β-ethylenically unsaturated mono- and/or dicarboxylic acid or its anhydride, or a monomer mixture containing at least one monomer and 0.01 to 10 mass parts of a radical initiator mixture are added to 100 mass parts of an ethylene polymer selected from ethylene-homo and/or linear ethylene copolymers, and graft-polymerized at reaction temperatures between 30 and 120° C. for a reaction time between 5 and 120 min. in a second stage, a mixture of 100 mass parts of the modified ethylene polymer obtained in the first solid phase stage, 150-4000 mass parts of an ethylene polymer- or polymer blend, and 150-4000 mass parts of an olefin elastomer are continuously fed to a reaction extruder, reacted at temperatures of between 160° and 260° C., wherein the graft-modified ethylene polymer blend having a degree of carboxylation between 0.05 and 1 mass-% is then continuously discharged. These products obtained on the basis of ethylene-home and/or linear ethylene copolymers products are intended, inter alia, for use as adhesion promoters.

It is the object of the present invention to provide, while avoiding the disadvantages described above, an adhesion promoter based on the functionalization of chemically resistant ethylene/ a, 3 -ethylenically unsaturated C₃- to C₁₂-olefin (diene) elastomers or propylene/C₂- and/or α, β-ethylenically unsaturated C₄- to C₁₂-olefin (diene) elastomers as well as cross-linked styrene/olefin/styrene or styrene/olefin block copolymers (TPES-V), in particular cross-linked styrene-ethylene/butane-styrene or styrene-ethylene/(ethylene)/propylene-styrene block copolymers.

The object is achieved according to the invention by a method as claimed in claim 1. The subject matter of the present invention is thus a process for preparing functionalized thermoplastic elastomers based on graft substrates. The graft substrates are selected from

-   -   olefin block copolymers of the composition of 80 to 98 mass-%         ethylene-12 to 20 mass-% of C₃- to C₁₂-olefin units, or     -   semi-crystalline propylene/ethylene- and/or C4- to C,₂-olefin         and/or C₄- to C₁₂-diene copolymers of the composition 50 to 98         mass-% propylene-/2 to 50 mass-% C₂- and/or C₄- to C₁₂- olefin         and/or C₄- to C₁₂ diene units, or     -   cross-linked styrene/olefin/styrene or styrene/olefin block         copolymers, in particular styrene-ethylenelbutene-styrene or         styrene-ethylene1(ethylene)!propylene-styrene block copolymers.

According to the invention,

-   -   from 0.1 to 15 mass parts of α, β-ethylenically unsaturated         compounds containing at least one functional monomer from the         series of functional groups or from 0.1 to 15 mass parts (MT) of         a monomer mixture containing at least one of these functional         monomers, and     -   from 0.01 to 10 mass parts of at least one initiator forming         free radicals with a 1-hour half-life temperature (T_(HWZ/1h))         between 50 and 200° C.         are added in the process to 100 mass parts of particulate graft         substrate in a fluid mixing reactor, i.e. in a         temperature-controlled mixer for fine-grained materials, which         ensures a free flowing powder bed, and polymerized at reaction         temperatures between 40° C. and the melting or softening         temperature of the graft substrate for a reaction time between         10 and 200 min in a solid-fluid phase, wherein a graft product         having a grafted functional monomer is produced by such a solid         phase functionalization, which is used as starting component for         further processing.

In further processing of the graft product, which advantageously contains a proportion between 0.05 and 12 mass-% of grafted functional monomer, 100 mass parts of the solid phase graft product, to which between 0.1 and 60 mass parts of at least one functional monomer or a monomer mixture containing between 0.1 and 60 mass parts of at least one functional monomer and between 0.01 and 20 mass parts containing at least one initiator forming free radicals with a 1-hour half-life temperature T_(HWZ/1h) between 80 and 240° C. are mixed in, together with 100 to 4000 mass parts of an unmodified olefin elastomer, are fed continuously by way of metering devices into the intake area of an extruder. The reactive extrusion is performed at temperatures above the melting or softening point of the olefin elastorner. A functionalized elastomer advantageously having a degree of functionalization between 0.1 and 5mass-% is continuously discharged at the end of the reactor.

As a specific embodiment of the invention. a process variant has been found advantageous wherein the solid phase functionalization of 100 mass parts of particulate graft substrate with between 0.5 and 15 mass parts of at least one functional monomer or with between 0.5 to 15 mass parts of a monomer mixture containing at least one functional monomer and 0.05 to 10 mass parts of at least one initiator forming free radicals with a 1 hour half-life temperature T_(HWZ/1h) at between 50 and 200° C. takes place at reaction temperatures between 50 and the melting or softening temperature of the graft substrate for a reaction time between 10 and 100 min, and wherein thereafter a graft product containing a proportion of between 0.1 and 10 mass-% grafted functional monomer is used as starting component. Here, 100 mass parts solid-phase graft product, to which between 0.5 and 50 mass parts of at least one functional monomer or between 0.5 and 50 mass parts of at least one monomer mixture containing a functional monomer and between 0.02 to 15 mass parts of at least one initiator forming free radicals with a 1-hour half-life temperature T_(Hyvvia) between 80 and 240° C. are admixed, are continuously fed together with 200 to 2000 mass parts of an unmodified olefin elastomer, preferably of the graft substrate used for solid phase functionalization, via metering devices into the intake section of a reaction extruder. The reactive extrusion is performed at temperatures between 160 and 300° C.. An elastomer, advantageously with a degree of functionalization between 02 and 4 mass-% is continuously discharged at the end of the reactor.

α, β-ethylenically unsaturated compounds containing carboxyl groups and/or derivatives selected from their anhydrides, mono- or di-esters, or mono- or di-amides are used as preferred functional monomers. Likewise, the functional monomers can advantageously also be selected from hydroxyl-, epoxy-, amino-, imido-, silane- or other α, β-ethylenically unsaturated compounds containing functional groups.

Of the carboxyl- and anhydride monomers usable as functionalizing agents, the so-called carboxylic monomers, maleic anhydride (MSA) and/or acrylic acid (AS) are particularly preferred. They are used alone or as a mixture with a co-monomer from the group of vinyl aromatics, preferably styrene. Other compounds preferably used as functional monomers are C1- to C₁₂-alkyl esters of acrylic or methacrylic acid, preferably methyl or ethyl or butyl acrylate or methyl methacrylate, which are used also either alone or as a mixture with a co-monomer from the group of vinyl aromatics, preferably styrene.

According to one embodiment of the aforedescribed process variant, compositions of from 99 to 20 mass-% functional monomer and from 1 to 80 mass-% of co-monomer are employed, preferably 95 to 50 mass-% of maleic anhydride (MSA) and/or acrylic acid (AA) and from 5 to 50 mass-% styrene.

The grafting initiated by radicals is, in order to achieve adequate degrees of functionalization and uniform grafting, advantageously performed by using a radical former or optionally a mixture of at least two different radical formers by using organic peroxides with 1-hour half-life temperatures (T_(HWZ/1h)) between 50 and 200° C. or 1-minute half-life temperatures (T_(HWZ/1min)) between 85 and 250° C., measured in 0.1 molar monochlorobenzene solution, with a concentration in relation to the entire graft substrate quantity between 0.001 and 5 mass-%, preferably between 0.02 and 2 mass-%.

Selected examples of useful radical initiators are dialkyl peroxy-dicarbonates with a 1-hour half-life temperature (T_(HWZ/1h)) between 60 and 70° C., such as dibutyl peroxy-dicarbonate (DBPOC) and dicetyl peroxy-dicarbonate (DCPOC) with a 1-hour half-life temperature (T) of 65° C., diauroyl peroxide (DLPO) with a 1-hour half-life temperature (T_(HWZ/1h)) of 80° C., dibenzoyl peroxide (DBPO) with a 1-hour half-life temperature (T_(HWZ/1h)) of 91 QC, tert-butyl peroxy-2-ethylhexanoate (TBPEH) with a 1-hour half-life temperature (T_(HWZ/1h)) of 91° C., tert-butyl peroxy-isobutyrate (TBPIB) with a 1-hour half-life temperature (T_(HWZ/1h)) of 98° C., 1,1-di-(tert-butylperoxy) cyclohexane (DTBPC) with a 1-hour half-life temperature (T_(HWZ/1h)) of 113° C., tea-butyl perbenzoate (TBPB) with a 1-hour half-life temperature (T_(HWZ/1h)) of 122° C., dicumyl peroxide (DCP) with a 1-hour half-life temperature (T_(HWZ/1h)) of 132° C., 2,5-dimethyl-2,5-di (tert-butylperoxy) hexane (DHBP) with a 1-hour half-life temperature (T_(HWZ/1h)) of 134° C., 2,5-dimethyl-2,5-di (tert-butylperoxy) hexyne (3) (DYBP) with a 1-hour half-life temperature (T_(HWZ/1h)) of 141° C., di-tert-butyl peroxide (TBP) with a 1-hour half-life temperature (T_(HWZ/1h)) of 141° C., cumene hydroperoxide (CHP) with a 1-hour half-life temperature (T_(HWZ/1h)) of 166° C. and tert-butyl -hydroperoxid (TBHP) with a 1-hour half-life temperature (T_(HWZ/1h)) of 185° C.

Taking into account the particular use, at least one additive selected from among known antioxidants and/or processing stabilizers, known fillers, reinforcing agents, fire-retardants and lubricant materials, extender oils and other additives can be added prior to further processing to the olefin elastomer functionalized according to the invention in the first stage, in the concentrations customary for the respective additives, as well as at least one polymer and/or elastomer component with a proportion of 1 to 90 mass-% in relation to the entire elastomeric molding material content.

Particularly advantageous is the use of processing stabilizers, wherein generally primary antioxidants are added based on sterically hindered phenol compounds with a proportion of 0.01 to 5 mass parts, preferably 0.1 to 2 mass parts, in relation to a elastomeric olefin copolymer or olefin block copolymer functionalized to 100 mass parts. Frequently, processing stabilizers are also used in the form of a combination of at least one primary and at least one secondary antioxidant, preferably a mixture consisting of 20 to 67 mass-% of a sterically hindered phenol and 80 to 33% mass-% of a phosphite compound.

The types IRGANOX® 1010 (pentaerythrityl tetrakis-[3-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate]), IRGANOX® 1330, IRGANOX' 1425 WL and IRGANOX® 3114 offered commercially by Ciba, as well as synergistic IRGANOX® mixtures of 20 to 50 mass-% of one of these primary antioxidants and 50 to 80 mass-% of the secondary antioxidant IRGAFOS® 168 (tris-(2,4-di-tert-butyl phenyl) phosphite), such as the type IRGANOX® 6561 prepared from 20 mass-% IRGANOX® 1010 and 80 mass-% IRGAFOS® 168, can be used as particularly suitable primary antioxidants,

Preferably, the functionalized thermoplastic elastomers according to the invention with a degree of functionalization between 0.1 and 5 mass-%, preferably with a degree of carboxylation between 0.2 and 4 mass-%, can be used as an adhesion promoter and/or adhesive for various substrates or multi-layer composites, preferably on and between plastic and/or metal surfaces.

Further details, features and advantages of the invention will become apparent from the following description of exemplary embodiments.

In the exemplary embodiments, the abbreviation MT is used for the unit “mass parts”. Accordingly, the unit mass parts per hour is abbreviated as MT/h.

Solid Phase Crafting EXAMPLE 1

In a temperature-controllable fluid mixing reactor equipped with an continuously variable stirrer from the company Reimelt Henschel, 100 MT powdery ethylene/α-olefin block co-elastomer of the type Infuse D 9007.15 with a density of 0.866 g/cm³, a melt flow rate (MFR) (190®C./2.16 kg) of 0.5 g/10 min, a Shore hardness A of 64 and an average particle diameter of 0.36 mm, hereinafter referred to as OBC 0.5, together with 1 MT dilauroyl peroxide, in the following designated by the abbreviation DLPO, and 2.8 MT maleic anhydride, hereinafter abbreviated as MSA, are fed at an internal reactor temperature of 20° C. Thereafter, the reaction mixture is dispersed in a nitrogen atmosphere at an agitation speed of 650 revolutions per minute [RPM] while simultaneously increasing the temperature with a heating rate of 2° C./min, and upon reaching the final reaction temperature T_(R1) of 90° C. maintained at T_(RI) over a time t_(R1) of 60 min.

The solid phase reaction is terminated by discharging the reaction product into the cooling mixer at a temperature of 20° C., from which it is taken out for determining the characteristic values shown in Table 1.

EXAMPLES 2 TO 13

In the following examples, the term melt flow rate is abbreviated as MFR and the to melt volume rate is abbreviated with MVR.

Other graft-functionalized olefin copolymers or olefin block copolymers are prepared according to the process flow described in Example 1 by using the following components:

Particulate elastomeric graft substrates:

Infuse D 9007.15: density=0.866 g/cm³, MFR 19° C./2.16 kg)=0.5 g/10 min, Shore A=64, with the designation description OBC-0.5, Infuse D 9817.15: density=0.877 g/cm³, MFR (190° C./2.16 kg)=15 g/10 min, Shore A=75, with the designation OBC-15 Versify 4000.01: density=0.888 g/cm³, MFR (230° C./2.16)=25 g/10 min, Shore A: 96 Notio PN-3560: density=0.866 g/cm³, MFR (230° C./2.16 kg)=6 g/10 min, Shore A: 70 Septon V 9461: density 0.863 g/cm³, MVR (320° C./2.16 kg)=7.2 cm³/10 minutes Septon V 9461-compound (for 100 MT Septon V 100 MT process oil and 27 MT PP): MFR (230° C./10 kg)=7 g/10 min, Shore A hardness=61.

All of the aforementioned graft substrates with the designation Infuse belong to the group of olefin block copolymers (OBC) having the composition 80 to 98 mass-% ethylene-/2 to 20 mass-% of C₃- to C₁₂-olefin units. The OBC are generally materials that are characterized by alternating HOPE and POE blocks. All of the aforementioned graft substrates with the designations Versify and Notio belong to the group of semi-crystalline propylene/ethylene- and/or C₄- to C₁₂-olefin copolymers and/or C₄- to C₁₂-diene copolymers having the composition 50 to 98 mass-% propylene-4 2 to 50mass-% of C₂- and/or C4- to C₁₂-olefin units and/or C₄- to C₁₂-diene units. All of the aforementioned graft substrates with the designation Septon belong to the group of cross-linked styrene/olefin/styrene- or styrene/olefin block copolymers.

Graft Monomers:

Maleic anhydride with the abbreviation MSA and acrylic acid with the abbreviation AS, hydroxyethyl acrylate with the abbreviation HEA, methyl methacrylate with the abbreviation MMA, and butyl acrylate with the abbreviation BA as well as styrene as co-monomer addition to the aforementioned functional monomers;

Peroxide Initiators:

Dilauroyl with the abbreviation DLPO, 2,5-dimethyl-2,5-di (tert-butylperoxy) hexane with the abbreviation DHBP, and dicetyl peroxidicarbonate with the abbreviation DCPOC, wherein these abbreviations are primarily used below.

While maintaining the charging and heating regime used in the Example 1, the reaction end temperature T_(R1), at a reaction time t_(R1) of 50 to 60 min and an agitation speed between 400 and 700 RPM and the monomer/initiator proportions introduced for 100 MT olefin elastomer are varied as essential parameters in accordance with the examples given in Table 1.

Table 1 lists the key process parameters for solid phase grafting:

-   -   Column 1: example number (Ex. No.)     -   Column 2: employed olefin-graft substrate, 100 MT     -   Column 3: type and concentration of the employed initiator in         [MT]     -   Column 4: monomer(s) with concentration specified in [MT]     -   Column 5: final reaction temperature T_(R1) in [° C.]     -   Column 6: volume melt rates, abbreviated as MVR. in [cm³/10 min]

Column 7: grafted monomer content, expressed as a degree functionalization FG in mass-%.

TABLE 1 Elastomer Initiator Monomer T_(R1) MVR Ex. No. 100 MT [MT] [MT] [° C.] [cm³/10 min] FG [wt.-%] 1 OBC 0.5 1.0 2.8 MSA 92   2.2 1.31 DLPO 1.0 styrene (190° C./21.6 kg) 2 OBC-15 1.0 4.0 HEA 90 18 2.51 DLPO 1.0 styrene (190° C./2.16 kg) 3 OBC-15 1.0 6.0 MMA 90 19 3.3 DLPO 0.5 BA (190° C./2.16 kg) 4 OBC-15 1.0 2.8 MSA 88   7.5 1.62 DLPO 0.5 styrene (190° C./21.6 kg) 5 OBC-15 1.0 5.0 BA 90 13 3.7 DLPO (190° C./2.16 kg) 6 Versify 0.5 5.0 AS 90 18 2.75 DLPO 1.0 styrene (230° C./2.16 kg) 7 Versify 0.3 4.5 AS 90 13 3.27 DCPOC 1.0 MSA (230° C./2.16 kg) 0.5 styrene 8 Notio 1.0 1.9 MSA 90   0.9 0.94 DLPO 0.2 styrene (230° C./2.16 kg) 9 Notio 0.7 1.5 MSA 90   1.0 0.77 DLPO 0.5 styrene (230° C./2.16 kg) 10 Notio 1.2 1.5 MSA 85   5.6 0.84 DCPOC 0.5 Styrene (230° C./5 kg)   11 Septon V 1.0 2.1 MSA 100 18 1.20 DLPO (320° C./21 kg)   12 Septon V 0.14 2.4 MSA 160 23 1.51 DHBP (320° C./21 kg)   13 Septon V- 0.5 2.4 MSA 80 16 0.64 Compound DCPOC (320° C./21 kg)  

Melt Drafting and Melt Compounding

As an advantageous embodiment of the inventive solution while using a particular concentration of solid phase functionalized product and after the addition of a further proportion of a functional monomer, an initiator and usually also a stabilizer, unmodified olefin elastomer is graft-functionalized in the molten state—in addition to the direct use of the elastomers functionalized in accordance with the inventive examples 1 to 13.

Preferably, the reactive extrusion, in particular the carboxylation or maleation, is performed in a twin-screw extruder.

EXAMPLE 14

The powdery solid phase product obtained in the first stage according to Example No. 1, which is included in the total mixture with 81.8 mass-% and to which 16 mass-% MSA and 1.2 mass-% DHBP and as a stabilizer 1.0 mass-% IRGANOX® B561, and mixture of 20 mass-% of the primary antioxidant, IRGANOX® 1010 and 80 mass-% of the secondary antioxidant IRGAFOS® 168 (manufacturer: Ciba) were added and dispersed, is fed via a metering scale at a feed rate of 5 MT/h to a twin screw kneader of the type ZSK 25 (L=42 D, temperatures ranging from 160 to 240° C., screw speed: 300 RPM) from the company Werner & Pfleiderer, equipped with an underwater granulator, abbreviation UWG. Simultaneously, granular OBC D 9000,00 with the characteristic value MVR (230° C./5 kg)=4 cm³/10 min, hereinafter referred to as OBC-4, are metered on a second scale 95 MT/h and added.

In accordance with the above-mentioned mass ratio of the solid phase graft product-mixture and OBC-4, the reactive extrusion is carried out at an average throughput of 100 MT/h. The melt temperature T_(M) is measured as 256° C. The smooth product strand emerging from the extruder nozzle is cut off by UWG. After drying the granules, the following parameters listed in Example 14 are determined:

MVR (230° C./5 kg)=5.3 cm³/10 min and degree of maleation CS_(ex)=0.64 mass-%.

EXAMPLES 15 to 20

By varying the recipe for melt grafting and melt compounding, i.e. the type of the components and their proportions, further melt grafting was carried out with the extrusion conditions described in Example 14, i.e. temperature, screw rotation speed and throughput, with the results being shown in Table 2.

In Table 2 are Listed:

Column 1 contains the numbers of the examples. Column 2 contains the concentration of used solid phase graft product with the corresponding example number from Table 1, indicated in mass parts per hour [MT/h]. Column 3 contains the type and concentration of added unmodified olefin elastomer, expressed in [MT/h]. In column 4, the average melt temperature T_(M) measured on the ZSK-nozzle is listed in [° C.]. In columns 5 to 7, the determined characteristic values are given, with column 5 containing the melt volume rate (MVR) (230° C./5 kg) in [cm³/10 min] and the qualitative strand assessment, selected from the assessments “smooth”, “almost smooth” and “rough”. Column 6 includes an indication of the respective degree of functionalization (CS), given in mass-%, also abbreviated as [wt.-%]. Column 7 contains information relating to the adhesive or peel strength (peel strength), specified in [N/mm].

The grafted portion CS_(ex) of MSA or AS, i.e. the degree of functionalization, also referred to as carboxylation or for MSA-grafting as degree of maleation CS_(ex) designated, was determined by way of reverse titration of the potassium hydroxide solution that was not neutralized by the proportion of carboxylic acid, i.e. MSA or AS, as follows: After treatment of the residue contained in the boiling methanol of a 2 g graft product sample over more than 6 h at 80° C. with a mixture composed of 100 ml of water-saturated xylene and 20 ml of 0.1 molar methanolic potassium hydroxide solution, titration is carried out with 0.1 molar hydrochloric acid following the adding of a few drops of a 1% methanolic phenolphthalein solution,

The grafted amount of HEA, BA and MMA—also shown as CS_(ex) values in Table 2—was determined by Near Infrared (NIR) analysis.

The melt volume rates, abbreviation MVR, just like the melt flow rates, abbreviation MFR, were determined according to ISO 1133.

Moreover, Table 2 also indicates a characteristic value for the adhesive strength in the form of the modified peel strength (peel strength) as a key property for the evaluation of the inventively functionalized olefin thermoplastic elastomers.

Table 2 also lists for comparison in the Examples 14A, 17A, 18A and 20A four graft-carboxylated olefin elastomers in the melt that were produced exclusively in the melt—without supplying an olefin elastomer grafted in the solid phase—, wherein in contrast to the examples according to the invention, the MSA, the initiator DHBP and also the stabilizer IRGANOX® B561 are fed not in the form of a mixture with the solid phase graft product, but instead are fed via the scale 2 into the extruder intake premixed in a portion of the respective unmodified olefin elastomer, According to the Example 14A, 95 MT/h of pure OBC D9000.00 was here fed via the first scale and a mixture consisting of 4 MT/h of pure OBC D9000.00, 0.9 MT/h MSA, 0.05 MT/h DHBP and 0.05 MT/h IRGANOX® B561 was fed via the second scale. A corresponding process occurred in the other comparative examples 17A, 18A and 20A.

0.05 mass-% of Irganox® 8561 were used in the examples for which no stabilizer concentrations are listed in the Table 2.

TABLE 2 Extruder operation Characteristic values Olefin Solid phase Monomer/ MVR Peeling elastomer Prod Table 1 Initiator T_(M) (230/5) CS_(ex) strength Ex. No. [MT/h] [MT/h] [MT/h] [° C.] [cm³/10′] [wt.-%] [N/mm] 14 95 OBC-4 4.09 No. 1 0.8 MSA 256 5.3 0.84 6.2 0.05 smooth DHBP 14A 99 OBC-4 — 0.9 MSA 258 2.3 0.65 4.1 0.05 almost DHBP smooth 15 92 OBC- 6.544 no. 1 1.28 MSA 262 14   0.92 7.0 15 0.096 smooth DHBP 0.08 stab. 16 95 OBC-4 4.01 No. 4 0.8 MSA 252 4.6 0.71 6.6 0.04 smooth DHBP 0.15 stab 17 95 Versify 4.09 No. 6 0.8 MSA 235 29   0.87 6.3 0.05 smooth DHBP 17A 99 Versify — 0.9 MSA 235 12   0.67 4.5 0.05 almost DHBP smooth 18 95 Notio 4.1 No. 8 0.8 MSA 238 6.7 0.73 6.0 0.05 smooth DHBP 18A 99 Notio — 0.9 MSA 240 2.3 0.65 4.1 0.05 rough DHBP 19 95 OBC-4 4.1 No. 2 0.8 HEA 261 1.6 0.91 5.3 0.05 smooth DHBP 20 90 OBC-4 8.2 No. 5 1.6 BA 258 1.2 1.25 6.5 0.1 DHBP almost 0.1 stab smooth 20A 98 OBC-4 — 1.8 BA 260 0.5 0.95 4.8 0.1 DHBP rough 0.1 stab.

As adhesion strength parameter is the peel strength determined in a material testing machine TC-FR010TH.A5V from the company Zwick GmbH & Co. on clamped samples composed of aluminum sheet strip/0.3 mm adhesive film/aluminum sheet strip composites (AI/HV/AI) with a pulling speed of 100 mm/min.

The granules obtained by UWG are extruded after drying into 0.3 mm thick sheets, cut into strips having a length of 80 mm and a width of 40 mm, and placed between two aluminum sheet strips with the same dimensions. The AI/HV/AI composites are then heat-treated in an oven at 180° C., and are afterwards measured after different storage times in the oven without application of additional weight and pressure.

The measurement is performed after a storage time of 8 min on the respective AI/HV/AI sample stripes that were cut into three pieces of 13.3 min×80 mm each. The peel strengths listed in Table 2 are the average values obtained from four AI/HV/AI composites and hence from a total of 12 single values for the test strips of a tested sample.

As the comparison of the characteristic values of graft products with the pure melt-functionalized products from the Examples 14A, 17A, 18A and 20A of Table 2 shows, the functionalized olefin elastomers produced according to the invention are characterized by high adhesive strengths with peel strengths ≧5 N/mm and by concurrent melt viscosities according MVR values (230° C./5 kg) between 1 and 30 cm³/10 min well and are thus well suited for many applications. In addition, it should be particularly emphasized that the high peel strengths of these new adhesion promoters are retained even after prolonged heat treatment.

LIST OF ABBREVIATIONS USED

-   AS Acrylic acid -   BA Butyl acrylate -   CHP Cumene hydroperoxide -   CS_(ex) Degree of maleation, carboxylation, grafted proportion -   DBPO Dibenzoylperoxide -   DBPOC Dibutyl peroxiclicarbonate -   DCP Dicumylperoxide -   DCPOC Dicetyl peroxidicarbona e -   DHBP 2,5-dimethyl-2,5-di (tert-butylperoxy) hexane -   DLPO Diauroylperoxide -   DTBPC 1,1-di-(tert-butylperoxy) -cyclohexane -   DYBP 2,5-dimethyl-2,5-di (tert-butylperoxy) hexyne (3) -   EOC Ethylene/octane (C₈) copolymers -   EPM Ethylene/propylene rubber -   FG Degree of functionalization -   HDPE High density polyethylene -   HEA Hydroxyethyl acrylate -   HV Adhesion promoter -   LDPE Low density polyethylene -   LLDPE Linear ethylene copolymers with a low C₃- to C₁₂-olefin     co-monomer fraction below 15 mass-% -   MFR Melt flow rates -   MMA Methyl methacrylate -   MSA Maisie anhydride -   MT Mass parts -   MT/h Mass parts per hour -   MVR Melt volume rate -   NIR Near Infrared -   OBC Olefin block copolymer -   POE Linear ethylene copolymers with a higher C₃- to C₁₂-olefin     co-monomer fraction above 15 mass-% -   TBHP tert-butyl hydroperoxide -   TBP Di-tent-butyl -   TBPB tent-butyl' perbenzoate -   TBPEH tert-butyl peroxy-2-ethylhexanoate -   TBPIB tert-butyl peroxy-isobutyrate -   T_(HWZ/1h) 1-hour half-life temperature -   T_(HWZ/1min) 1 minute half-life temperature -   T_(M) Melt temperature -   TPE-S Styrene/diene segment/styrene or styrene/diene segment-block     copolymers -   TPES-V Styrene/olefin/styrene-block copolymers -   T_(R1) Reaction end temperature -   t_(R1) Time (for holding the reaction et d temperature T_(R1)) -   RPM Revolutions per minute -   UWG Underwater granulation 

1. A process for preparing functionalized thermoplastic elastomers based on graft substrates selected from olefin block copolymers with the composition 80 to 98 mass-% of ethylene-/2 to 20 mass-% of C₃- to C1₂-olefin units, or semi-crystalline propylene/ethylene and/or C₄- to C₁₂-olefin and/or C₄- to C₁₂-diene copolymers of the composition 50 to 98 mass-% of propylene-/ 2 to 50 mass-% of C₂- and/or C₄- to C₁₂ olefin and/or C₄- to C₁₂ and/or C₄- to C₁₂-diene units, or cross-linked styrene/olefin/styrene- or styrene/olefin block copolymers, wherein in a fluid mixing reactor, i.e. in a temperature-controllable mixer for fine-grained materials, which ensures a free flowing powder bed, 0.1 to 15 mass parts of at least one functional monomer from the series of functional groups containing α, β-ethylenically unsaturated compounds or from 0.1 to 15 mass parts of a monomer mixture containing at least one of these functional monomers, and 0.1 to 10 mass parts of at least one initiator forming free radicals with a 1-hour half-life temperature (T_(HWZ/1h)) between 50 and 200° C. are added to 100 mass parts of particulate graft substrate and polymerized at reaction temperatures between 40° C. and the melting or softening temperature of the graft substrate for a reaction time between 10 and 200 min in the solid-fluid phase, whereby by such a solid state functionalization a graft product possessing a grafted functional monomer is produced which is used as starting component for further processing, wherein during further processing of the graft product 100 mass parts of a solid phase graft product, to which between 0.1 and 60 mass parts of at least one functional monomer or of a monomer mixture containing at least one functional monomer and between 0.01 and 20 mass parts of at least one initiator forming free radicals with a 1-hour half-life temperature (T_(HWZ/1h)) 80-240° C. were admixed, together with 100 to 4000 mass parts of an unmodified olefin elastomer, are continuously fed into the feed area of an extruder via metering devices, the reactive extrusion is carried out at temperatures above the melting or softening point of the olefin elastomer, and a functionalized elastomer is continuously discharged at the reactor end.
 2. The method according to claim 1, wherein the solid phase functionalization of 100 mass parts of particulate graft substrate is carried out by means of 0.5 to 15 mass parts of at least one functional monomer or a monomer mixture containing at least one functional monomer and 0.05 to 10 mass parts of at least one initiator forming free radicals with a 1-hour half-life temperature (T_(HWZ/1h)) between 50 and 200° C. at reaction temperatures between 50° C. and the melting or softening temperature of the graft substrate for a reaction time between 10 and 100 min, and that subsequently a graft product having a proportion between 0.1 and 10 mass-% of a grafted functional monomer is used as a feed component, wherein 100 mass parts solid phase graft product, to which between 0.5 and 50 mass parts of at least one functional monomer or at least one monomer mixture containing a functional monomer and 0.02 to 15 mass parts of at least one initiator forming free radicals with a 1-hour half-life temperature (T_(HWZ/1h)) between 80 and 240° C. have been admixed, are fed continuously into the intake of a reaction extruder together with 200 to 2000 mass parts of an unmodified olefin elastomer via metering devices, wherein the reactive extrusion is carried out at temperatures between 160 and 300° C. and an elastomer is continuously discharged at the reactor end.
 3. The method according to claim 1, wherein α, β-ethylenically unsaturated compounds containing carboxyl groups and/or the derivatives selected from their anhydrides and/or mono- or diesters and/or mono- or diamides are used as functional monomers.
 4. The method according to claim 1, wherein the functional monomers are α, β-ethylenically unsaturated compounds, which contain, as functional groups, hydroxyl-, epoxy-, amino-, imido- or silane groups.
 5. The method according to claim 3, wherein maleic anhydride (MA) and/or acrylic acid (AS) alone or as a mixture with a co-monomer from the group of vinyl aromatics are used as functional monomers.
 6. The method according to claim 3, wherein The C₁- to C₁₂-alkyl esters of acrylic or methacrylic acid alone or as a mixture with a co-monomer from the group of vinyl aromatics are used as functional monomers.
 7. The method according to claim 5, wherein compositions of 99 to 20 mass-% of a functional monomer and 1 to 80 mass-% of a co-monomer are used.
 8. The method according to claim 1, wherein the radical-initiated grafting using a radical former or a mixture consisting of at least two different free-radical formers is performed using organic peroxides with 1-hour half-life temperature (T_(HWZ/1h)) between 50 and 200° C. or a 1-minute half-life temperature (T_(HWZ/1min)) between 85 and 250 in a concentration between 0.001 and 5 mass-% in relation to the entire graft substrate quantity.
 9. The method according to claim 8, wherein dialkyl peroxydicarbonates with a 1-hour half-life temperature (T_(HWZ/1h)) between 60 and 70° C., diauroylperoxid (DLPO) with a 1-hour half-life temperature (T_(HWZ/1h)) of 80° C., dibenzoyl peroxide (DBPO) with a 1-hour half-life temperature (T_(HWZ/1h)) of 91° C., tert-butyl peroxy-2-ethylhexanoate (TBPEH) with a 1-hour half-life temperature (T_(HWZ/1h)) of 91° C., tert-butyl peroxy-isobutyrate (TBPIB) with a 1-hour half-life temperature (TH_(HWZ/1h)) of 9820 C., 1,1-di-(tert-butylperoxy) cyclohexane (DTBPC) with a 1-hour half-life temperature (T_(HWZ/1h)) of 113° C., tert-butyl perbenzoate (TBPB) with a 1-hour half-life temperature (T_(HWZ/1h)) of 122° C., dicumyl peroxide (DCP) having a 1-hour half-life temperature (T_(HWZ/1h)) of 132° C., 2,5-dimethyl-2,5-di (tert-butylperoxy) hexane (DHBP) with a 1-hour half-life temperature (T_(HWZ/1h)) of 134° C., 2,5-dimethyl-2,5-di (tert-butylperoxy) hexyne (3) (DYBP) with a 1-hour half-life temperature (T_(HWZ/1h)) of 141° C., di-tert-butyl peroxide (TBP) having a one-hour haft-life temperature (T_(HWZ/1h)) of 141° C., cumene hydroperoxide (CHP) with a 1-hour half-life temperature (T_(HWZ/1h)) of 166° C. and tert-butyl hydroperoxide (TBHP) with a 1-hour half-life temperature (T_(HWZ/1h)) of 185° C. can be used as radical formers.
 10. The method according to claim 1, wherein at least one additive selected from antioxidants and/or processing stabilizers, fillers, reinforcement agents, flame retardants, and lubricants as well as extender oils in concentrations customary for the respective additives, and at least one polymer and/or elastomer component with a proportion of 1 to 90 mass-% based on the entire elastomeric extruded mass is added to the functionalized olefin elastomer.
 11. The method according to claim 10, wherein primary antioxidants based on sterically hindered phenol compounds with a proportion of 0.01 to 5 mass parts in relation to an elastomeric olefin copolymer or olefin block copolymer functionalized to 100 mass parts are added as processing stabilizers.
 12. The method according to claim 10, wherein processing stabilizers in the form of a combination of at least one primary and at least one secondary antioxidant are used.
 13. (canceled)
 14. (canceled)
 15. (canceled)
 16. (canceled) 